RocketPoxy G5000 - High Strength Epoxy - 8oz with Black Pigment & 10 Mixing Sticks

$12.50
$12.50
$12.13
(You save $0.37 )
(No reviews yet) Write a Review
SKU:
RPG5000V8OZ
Weight:
1.50 LBS
Shipping:
Calculated at Checkout

G5000 is a two component filled epoxy with high strength bonds for joining fiberglass and carbon fiber composites with extremely high shear strengths. It also has excellent adhesion to metals, plastics, woods, and ceramics as well. Cures to a very high strength bond that is also nonbrittle to eliminate flexing cracks. Easy to mix 1 to 1 ratio by weight and volume. Mixes to a smooth creamy paste that when applied eliminates drips, sagging, or runoff. Does not require any thickening or strength additives as epoxy is ready to use as supplied. The adhesive cures relatively quickly and can be handled within a few hours. Cures to an easy to paint off white color but pigment can be easily added to provide almost any color desired. 

It has excellent mechanical properties, high shear and peel strength, great adhesion, good chemical and environmental resistance, good thermal shock resistance and very low shrinkage.  It has low exotherm during cure for filling large mass voids. 

Uses: Joining and bonded fiberglass, carbon fiber, composites, any where a high strength non-brittle bond is needed. Great for attaching composite rocket fins, bulk plates, nose cone hardware and especially for professional grade fin fillets. 

Mixing and Cure Instructions: Ratio by weight: Resin 100 Hardener 100 Ratio by volume: Resin 100 Hardener 100 Pot life (100 gram mass at 72°F) = 30 to 40 minutes ASTM D2471 Handling time = 3 to 4 hours Full cure = 6 to 8 hours 

Physical Properties (@ 72°F/ 22°C): Color Off white but can be pigmented to black or any color. Shore “D” hardness 85 ASTM D2240 Viscosity Resin Paste Viscosity Hardener Paste Viscosity Mixed Paste Specific gravity, Resin 1.52 Specific gravity, Hardener 1.48 Specific gravity mixed 1.50 Tensile strength 7,600 psi ASTM D638 Compression strength 14,800 psi ASTM D695 Elongation at break % 6.3% ASTM D638 Typical operating temperature -50°F to 175°F Maximum use temperature 225°F (107°C) Deflection temperature 150°F (66°C) ASTM D648 Shelf Life 1-1/2 Years Notice: This information is presented to assist the user in determining whether our products are suitable for his intended use. The user assumes all risks and liability in connection therewith. No warranty or representation express or implied shall apply to these products. Seller’s only obligation shall be to replace quantity of this product which has proven to not substantially comply with the data presented. Seller shall not be responsible for property loss or damage direct or consequential arising out of use of this product(s) or inability to use this product(s). See material safety data sheet before using.

DIRECTIONS FOR USE G5000 HIGH STRENGTH EPOXY 

Preparation:
 All surfaces being bonded should be free of mold release, oil, grease, and dirt. Sand with 60 to 80 grit to rough up the areas to be bonded. A well roughed up surface will greatly increase the surface area the epoxy will bond to and greatly increase the bond strength. 

Mixing: Measure out equal parts of A and B by weight or “eyeball” by volume. Mix together until a uniform color and consistency is reached. Mix for approximately 1 to 2 minutes scraping the sides and bottom of containers to avoid any unmixed material. At this time a pigment color can be added to color the epoxy. Mix in a few drops or squirts of the pigment at a time until the desired color and shade is reached. Mix as completely as possible. 

Application: Apply mixed epoxy to the area to be bonded. Even though the material is a paste it will flow a little bit after applied if used right away. If you do not want any material flow at all when applied this can be accomplished by waiting approximately 15 to 30 minutes after epoxy is mixed before using, this will allow the epoxy to stiffen up and retard flow. If you need to work the epoxy after applied such as a fillet on a rocket fin or repairing a hole in a tube use isopropyl alcohol, this can be applied to a tool or a finger to push, move, and/or smooth out the curing epoxy. Also isopropyl alcohol can be used to thin the epoxy and also clean up any uncured epoxy. 

Curing: Use a clamp, jig, or improvised device to prevent movement during initial curing time. Parts can be handled in about 3 to 4 hours if necessary, but full curing time is about 6 to 8 hours and bonded parts can be put into light service at this time. 24 hours cure is recommended for obtaining the highest strength. Curing can be speed up by using an oven to place the bonded parts in, full curing can be obtained in 1 hour at 140 Degrees F. Also heat can be applied to the mixed material before being bonded to accelerate the curing time, a device such as a heat gun can be used to warm up the epoxy in a cup prior to being applied. Also if you encounter air bubbles in an surface area such as a fin fillet running a heat gun quickly above them will help eliminate them. Notice: This information is presented to assist the user in determining whether our products are suitable for his intended use. The user assumes all risks and liability in connection therewith. No warranty or representation express or implied shall apply to these products. Seller’s only obligation shall be to replace quantity of this product which has proven to not substantially comply with the data presented. Seller shall not be responsible for property loss or damage direct or consequential arising out of use of this product(s) or inability to use this product(s). See material safety data sheet before using.